TERNALLOY TR
Saldflux - Brazing

When there are large inequalities between the sizes of the components composing the joint some- times occurs a joint failure re- sulting from thermally inducted stress. Perhaps the best known example of this probelm is when large pieces of tungsten carbide are brazed to steel backing pieces.

Braze filler composites that have a core of copper with a coating of filler metal on both surfaces (1:2:1) are frequently used to reduce the risk of crack- ing (sandwiched or trifoil material).

Name Composition SF Melting
point °C
Working
temperature °C
agcuznmnni
TERNALLOY 49 TR 49 27,5 20,5 2,5 0,5 SF-W4490CU c.a. 670 - 690 °C c.a. 690° C
Registered Office and Offices:
Via Friuli, 5
20072 Fizzonasco di P.E. - Milano - Italy
TEL. +39 02 907 81 812
FAX. +39 02 907 84 933

Warehouse:
Via Privata Vico Veneto, 32/5
20072 Fizzonasco di P.E. - Milan - Italy

Factory:
Via Martiri Della Resistenza, 6
20072 Fizzonasco di P.E. - Milano - Italy
COMPANY PROFILE


saldflux uses cookies to offer you a better service. By continuing, you agree to these cookies. Ok